TINGKAT KEKERASAN PERMUKAAN RESIN KOMPOSIT AKIBAT MASA KEDALUWARSA MATERIAL
Yuvika Intan Ristian Putri
Muhammad Dian Firdausy
- Indonesia
Departemen Dental Material Fakultas Kedokteran Gigi Universitas Islam Sultan Agung Semarang
Niluh Ringga Woroprobosari
- Indonesia
Departemen Radiologi Forensik Fakultas Kedokteran Gigi Universitas Islam Sultan Agung Semarang
(*) Corresponding Author
Background: Aplication of composites resin in relatively small amount as a restorative material often causing the material reaches its expiry date before all of the material can be used. Composites resin that have passed the expiry date would affect charateristic of the material. The aim of this study was to investigate surface hardness difference of composite resins based on material expiration date.
Methods: This research was an experimental laboratory using post test only with control group design. Samples for this research were 27 divided into 3 groups based on its expiration date (2016, 2018 and 2019). The surface hardness was measured by Shore D Hardness. The result of this research were tested with One Way Anova and Post Hoc test LSD.
Result: The lowest surface hardness result was measured on group 1 (81.02
SHD) and the highest was group 3 (94.72 SHD). The result of One Way Anova test showed that there was signifcant differences in all groups (p<0.05). Post Hoc LSD test showed difference signifcantly between each groups.
Conclusion: It can be concluded that there was signifcant difference of composite resins surface hardness based on material’s expiration date
Methods: This research was an experimental laboratory using post test only with control group design. Samples for this research were 27 divided into 3 groups based on its expiration date (2016, 2018 and 2019). The surface hardness was measured by Shore D Hardness. The result of this research were tested with One Way Anova and Post Hoc test LSD.
Result: The lowest surface hardness result was measured on group 1 (81.02
SHD) and the highest was group 3 (94.72 SHD). The result of One Way Anova test showed that there was signifcant differences in all groups (p<0.05). Post Hoc LSD test showed difference signifcantly between each groups.
Conclusion: It can be concluded that there was signifcant difference of composite resins surface hardness based on material’s expiration date
Keywords: Microhybrid composites resin; Surface hardness; Material’s expiration date
- Tulenan, D.M.P., Wicaksono, D.A. & Ratulangi, U.S. 2014. Gambaran Tumpatan Resin Komposit Pada Gigi Permanen Di Poliklinik Gigi Rumkital Dr.Wahyu Slamet. J e-GiGi (eG). 2(2).
- Anang, D.Y., Mariati, N.W. & Mintjelungan, C.N., 2015. Penggunaan Bahan Tumpatan Di Rumah Sakit Gigi Dan Mulut Pspdg Fakultas Kedokteran Unsrat Pada Tahun 2014. J e-GiGi (eG). 3:3–6.
- Anusavice, PhD, K.J., Rawls, PhD, R. & Shen, PhD, C., 2013. Phillip’S Science of Dental Materials. ed ke-12. Missouri: Elsevier, pp. 277- 304
- Sitanggang, P., Tambunan, E., Wuisan, J. 2015. Uji Kekerasan Komposit Terhadap Rendaman Buah Jeruk Nipis (Citrus Aurantifolia). J e-GiGi (eG). 3:229–234.
- Garcia, L. da F.R., Rego Roselino, L. de M. & Pires de Souza, Fernanda de Carvalho Panzeri Consani, S. 2010. Evaluation Of The Conversion Degree, Microhardness, And Surface Roughness Of Composite Resins Used After Their Expiration Date. www.agd.org, pp.262–267.[19 April 2017].
- Talreja, N., Shilpy, S., ND, S. 2017. Comparative Evaluation of Bond Strength and Microleakage of Standard and Expired Composite at Resin – Dentin Interface : An in vitro Study. IJCPD.
- (1):1–4.
- Pasril, Y., Pratama, W.A. 2013. Perbandingan Kekuatan Tekan Resin Komposit Hybrid Menggunakan Sinar Halogen Dan LED Comparison of Compressive Strength Hybrid Composite Resin Using Halogen and LED Light. IDJ. 2(2):83–90.
- Tirapelli,C., Carvalho,F., Panzeri,H. 2004. Radiopacity and Microhardness Changes and Effect of X-ray Operating Voltage in Resin-Based Materials before and after the Expiration date. www.scielo.br. pp. 409-412.[1 Februari 2018]